CA 2750014
In this method, the inner surface of a metal pipe containing, by mass percent, 20 to 55% of Cr and 20 to 70% of Ni is subjected to mechanical treatment, the metal pipe is subjected to heat treatment such as to be held in a temperature range of 1050 to 1270°C for 0.5 to 60 minutes, and thereby an oxide scale layer consisting mainly of Cr is formed on at least the inner surface of the metal pipe. A metal pipe excellent in carburization resistance and coking resistance in a carburizing gas environment can be obtained by the method.
Cette invention concerne un procédé de production d'un tube métallique présentant une excellente résistance à la carburation et à la cokéfaction en atmosphère gazeuse carburante. La surface interne d'un tube métallique contenant de 20 à 55 % en masse de Cr et de 20 à 70 % en masse de Ni est soumise à un traitement mécanique suivi d'un traitement thermique dans une plage de températures allant de 1 050 à 1 270 ºC pendant 0,5 à 60 minutes. Ainsi, une couche de calamine contenant principalement du Cr est formée au moins sur la surface interne du tube métallique.
Nishiyama Yoshitaka
Toyoda Masatoshi
Ueyama Masaki
Gowling Lafleur Henderson Llp
Sumitomo Metal Industries Ltd.
LandOfFree
Method for manufacturing metal pipe does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for manufacturing metal pipe, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for manufacturing metal pipe will most certainly appreciate the feedback.
Profile ID: LFCA-PAI-O-1560483