ABSTRACT A low temperature LPCVD process for co-depositing metal and silicon to form metal silicide on a surface such as the surface of a semiconductor integrated circuit wherein the metal is selected from the group consisting of tungsten, molybdenum, tantalum and niobium. A reactor which contains the surface is maintained at a temperature of about 500°-700°C. The reactor is purged by the successive steps of introducing an inert gas into the reactor, introducing a reducing atmosphere into the reactor and introducing hydrogen chloride gas into the reactor. Silane is then introduced into the reactor such that a base layer of polysilicon is formed on the surface. Then, while maintaining silane introduction to the reactor, metal chloride vapor is simultaneously introduced into the reactor such that metal and silicon are co-deposited on the polysilicon as metal silicide.
407063
Fairchild Camera And Instrument Corporation
Smart & Biggar
LandOfFree
Method for lpcvd co-deposition of metal and silicon to form... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for lpcvd co-deposition of metal and silicon to form..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for lpcvd co-deposition of metal and silicon to form... will most certainly appreciate the feedback.
Profile ID: LFCA-PAI-O-1241200