Moldable ceramic composition and process for fine diameter...

Details Moldable ceramic composition and process for fine diameter... Moldable ceramic composition and process for fine diameter...

C - Chemistry, Metallurgy

08

L

25/131, 400/5058

C08L 23/18 (2006.01) C04B 35/622 (2006.01) C04B 35/634 (2006.01) D01F 9/08 (2006.01)

Patent

CA 2016457

A thermoplastic ceramic molding composition comprised of about 40 to 70 volume percent of a binder, consisting essentially of an organic acid containing from 12 to 26 carbon atoms per molecule and a polyisobutylene polymer having a molecular weight between about: 8,700 and 135,000, and about 30 to 60 volume percent of a ceramic powder is disclosed. The molding composition can be thermoplastically extruded into elongate ceramic bodies that can be uniformly elongated many times the original length of the ceramic body to form, for example, very fine diameter fibers or filaments suitable for sintering into a polycrystalline ceramic fiber or filament having a very fine diameter.

Affiliated with

Also associated with

Rating

Moldable ceramic composition and process for fine diameter... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Moldable ceramic composition and process for fine diameter..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Moldable ceramic composition and process for fine diameter... will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFCA-PAI-O-1637048