A method for coating finely divided material with titania is disclosed. The method involves the fluidization of the finely divided material in an inert carrier gas containing vaporized titanium isopropoxide. The isothermal fluidized bed is kept at a temperature equal to or below approximately 300°C. The vaporized titanium isopropoxide reacts to form a coating of titania on the surfaces of the particles within the fluidized bed. The greatest coating efficiency occurs when the fluidized bed is kept at approximately 300°C for approximately the first 10 minutes of the reaction and thereafter at approximated 250°C. The titania coating process is particularly useful for electroluminescent phosphors such as copper doped zinc sulfide phosphor. The titania coated electroluminescent phosphors are relatively insensitive to moisture. Lamps made from the coated electroluminescent phosphor are also relatively insensitive to moisture.
Gte Laboratories Incorporated
Gte Products Corporation
R. William Wray & Associates
LandOfFree
Process for coating finely divided material with titania and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for coating finely divided material with titania and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for coating finely divided material with titania and... will most certainly appreciate the feedback.
Profile ID: LFCA-PAI-O-1810790