Patent
CA 2148406
Process for producing very pure platinum materials dispersion-reinforced with Y2O3 and having high strength and extensibility, even in the temperature range > 800°C, from platinum powder by mechanical alloying, which comprises the process steps - preparing platinum powder of high purity and low particle size of from 2 to 10 µm, - introducing and dispersing Y2O3 particles < 1 µm in the platinum powder by milling in a platinum vessel using milling media of zirconium oxide, - degassing the milled product under a vacuum of better than 10-3 mbar and with an increase in tem- perature to at least 1200°C in a platinum capsule for a period of up to 48 hours, - gastight welding of the evacuated capsule and hot isostatic pressing at 1350°C and 200 MPa to give blocks of compact dispersion-reinforced platinum having a density of 100 %, - producing semi-finished parts and foils from these dispersion-reinforced platinum materials, these parts and foils having - a platinum purity of at least 99.95 %, - a tensile strength Rm from 300 to 350 MPa, - an extensibility A of 15 - 25 % and a - grain stability up to 1400°C.
Disam Joachim
Edtmaier Christian
Jangg Gerhard
Schreier Gerhard
Zbiral Johannes
Marks & Clerk
Schott Glaswerke
LandOfFree
Process for producing very pure platinum materials,... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for producing very pure platinum materials,..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for producing very pure platinum materials,... will most certainly appreciate the feedback.
Profile ID: LFCA-PAI-O-1556919